Product Overview
ZA0211 ABS is an acrylonitrile-butadiene-styrene (ABS) copolymer resin produced by Zhejiang Petrochemical Co., Ltd. This material is a high-flow injection molding grade with a melt flow rate of 20 g/10 min (220 ℃, 10 kg), exhibiting excellent melt filling capability. Its core functional value lies in balancing processing efficiency with product rigidity, making it suitable for industrial manufacturing scenarios that require optimized molding cycles and production rates. This grade is specifically designed for high-speed injection molding processes and is widely used in the production of electronic and electrical housings and consumer product components.
Technical Data Sheet (TDS)
Physical Properties
| Physical Properties | Test Value | Test Unit | Test Standard |
| Melt Flow Rate, Mass (220 ℃, 10 kg) | 20 | g/10 min | GB/T 3682.1 |
| Density | 1.035 | g/cm³ | ASTM D792 |
| Mold Shrinkage | 0.4-0.7 | % | ASTM D955 |
Mechanical Properties
| Mechanical Properties | Test Value | Test Unit | Test Standard |
| Tensile Strength (50 mm/min) | 43 | MPa | GB/T 1040.2 |
| Flexural Strength (2 mm/min) | 68 | MPa | GB/T 9341 |
| Flexural Modulus (2 mm/min) | 2400 | MPa | GB/T 9341 |
| Izod Impact Strength, Notched (23 ℃, 4 mm) | 23 | kJ/m² | GB/T 1043.1 |
Thermal Properties
| Thermal Properties | Test Value | Test Unit | Test Standard |
| Heat Deflection Temperature, Unannealed (1.8 MPa) | 83 | ℃ | GB/T 1634.2 |
| Vicat Softening Point (4 mm) | 95 | ℃ | GB/T 1633 |
| Flammability Rating (1.5 mm) | HB | — | UL 94 |
Disclaimer: The technical specifications for Zhejiang Petrochemical ZA0211 presented herein are derived from data issued by Zhejiang Petrochemical Co., Ltd. or certified third-party testing institutions. While we have made every effort to ensure the accuracy of the information provided, we assume no liability for any consequences arising from the use of ZA0211 based on these data. Given the variables involved in processing conditions, we strongly recommend conducting thorough trials of ZA0211 under your specific operational environment prior to final material selection.
Logistics & Supply Standards
This product is packaged in standard 25 kg multi-layer kraft paper bags. We maintain consistent stock at major ports and inland logistics hubs to ensure supply chain stability. The average lead time for standard orders depends on the Incoterms and destination customs clearance efficiency and can usually be arranged for shipment upon order confirmation. As a non-hazardous chemical, ZA0211 ABS supports consolidated shipping with other general plastic raw materials, helping customers optimize total logistics costs and warehouse space utilization.
Compliance & Quality Commitment
We ensure that all supplied ZA0211 ABS complies with the requirements of the RoHS Directive and REACH regulations regarding restricted substances. Each batch is accompanied by complete quality management documentation, including a Technical Data Sheet (TDS), Safety Data Sheet (SDS), and Certificate of Analysis (COA). We have established a strict batch traceability mechanism to ensure that data from polymerization, packaging, to final delivery is fully verifiable, meeting the compliance requirements of downstream processors for raw material traceability.
Sustainability & ESG
As a thermoplastic polymer, ABS possesses physical recycling and reuse properties. ZA0211 manufacturing implements process controls aimed at reducing energy consumption and volatile organic compound (VOC) emissions. We encourage customers to categorize, recycle, and reprocess sprues and rejects during processing to support the development of a circular economy. Furthermore, the product’s supply chain management adheres to industry environmental standards, committing to reducing the environmental footprint throughout the product life cycle in line with current green supply chain trends.
Frequently Asked Questions (FAQs)
Q1: What are the recommended drying parameters for ZA0211 prior to processing?
A1: ABS material is hygroscopic. To prevent surface defects such as silver streaks, bubbles, or uneven gloss during injection molding, drying is recommended before processing. The recommended process is to treat the material in a hot-air circulating dryer at 80-85°C for 2-4 hours, ensuring the moisture content is below 0.1%. Duration may be fine-tuned based on the humidity of the storage environment.
Q2: What should be noted regarding mold design for the high-flow characteristics of ZA0211?
A2: Due to its high melt flow rate (20 g/10min), the melt fills quickly, which may lead to jetting or gas entrapment. It is recommended to increase the depth of the venting channels in the mold design (typically 0.02-0.03mm) and use fan or tab gates to control shear rates. Additionally, higher flowability may increase the risk of flash, requiring strict control of clamping force and injection pressure.
Q3: Does this material meet specific flame retardancy or environmental certifications for the electronics and electrical industry?
A3: The base flame retardancy rating of ZA0211 is UL 94 HB (1.5mm). If the end-use application requires V-2 or V-0 ratings, modification with flame retardants is typically necessary. Regarding environmental compliance, the base resin complies with RoHS and REACH standards. For specific halogen-free requirements, we recommend requesting the corresponding third-party test reports to confirm the formulation status.